Product categories

More »

Stainless Steel

Stainless Steel specifications held in the austenitic, martensitic and precipitation hardening varieties. Stocks are held in British Standard and International standards. Below is listed our most commonly supplied grades; please contact our sales office. Also stock is 301 stainless spring temper rolled strip.

Hi-Steel HSLA-80

Hi - Speed, high Speed Steel Tool Steel (made) : highly processed into the Tool Steel, carbon content high, while containing cr quantity is low (about 4%), reason burnish of Steel surface gloss darker, after heat can reach by HRc62 high hardness, resistance to rust performance not on a roll.

Mould Steel

Steel mould and Steel mould suppliers, global delivery, stock supply Steel mould steels.

Heat Resistant Steel

Heat resistant steel. AS Orlov Izobret. Mashinostr. 3, 48-49, 7/2000. The purpose of this work was to increase plasticity of heat resistant steel after aging at the 500-1300 deg C temperature and to improve its operational reliability.

Tool Steel

Comprehensive stocks held of tool steel, including hot work, cold work and plastic mould tool steel specifications. Below we detail our most common grades. Other British Standard and international special steels and tool steels are also available, please contact our sales office.

Ball Bearing Steel

Supplies Ball bearing steel of all types, along with carbon steel and specialty balls, to OEM's around the world. Also offers platinum balls, brass balls, gold, titanium, aluminum, carbon and plastic balls.

Spring Steel

Carbon spring steel is held in a wide range of sizes. Detailed below are our most common specifications. Carbon steel strip and spring steel sheet is available most commonly in the hardened and tempered condition, though certain sizes are available in the annealed condition. Round and flat bar is stocked in the as rolled condition. Most spring steel specifications are held to British Standard steel specifications including BS1449 & BS970.

Alloy and Carbon Steel

Alloy steel is steel alloyed with a variety of elements in total amounts of between 1.0% and 50% by weight to improve its mechanical properties. Alloy steels are broken down into two groups: low alloy steels and high alloy steels. The difference between the two is somewhat arbitrary: Smith and Hashemi define the difference at 4.0%, while Degarmo, et al., define it at 8.0 %.[1][2] Most commonly, the phrase "alloy steel" refers to "low alloy" steels.

News

More »

Enterprise email

Home » Tool Steel » Product introduction

AISI S7 Tool Steel

  • Numbers: 2011030512
  • Model: AISI S7
  • Producers: China
  • Update time: 2011.03.05
  • Browse:

Product Description:

 Tool Steel

AISI S7 Shock Resistant Tool Steel

  • (Machine finish) T & B WITH SAW-CUT EDGES
  • (Machine finish) FOUR SIDES

DESCRIPTION

Shock steel with exceptional impact properties. Since it hardens in air, it is safe and stable in heat treatment. Most remarkable characteristic is its versatility. Used widely for medium-run cold-work tools and dies, for plastic-molding dies, for shear blades, for medium hot-work dies, for master hobs, and for component parts of many Products.

ADVANTAGES

  • Good machinability
  • Maximum shock resistance
  • Air hardening
  • Cold & medium hot-work characteristics

TYPICAL ANALYSIS

CARBON ………………..0.50 SILICON …………………0.25

MANGANESE ………….0.70 CHROMIUM ……………3.25

MOLYBDENUM ……….1.40

HEAT TREATMENT

FORGING ………………………………..Preheat 1200°F to 1300°F; forge at 2000°F to 2050°F, stop at

1700°F and cool slowly

NORMALIZING ………………………...Do not normalize

ANNEALING ……………………………1500°F to 1550°F, cool slowly to 1000°F, air-cool, Brinell 197 max

PREHEATING ……………………………1200°F to 1300°F, prior to hardening

HARDENING …………………………….1725 °F. Quench in air if cross-section is 2-1/2 in. or smaller;

sections 2-1/2 in. to 6 in. should be oil-quenched to black

(1000°F) followed by air-cooling to 150°F; larger cross-sections

should be oil-quenched to 150°F.

TEMPERING ……………………………...400° F minimum. Double tempered is recommended.

MACHINABILITY

Rated at 95 annealed to Brinell 197 max., as compared to a rating of 100 for a one percent carbon Tool Steel.

DIMENSIONAL STABILITY

Can be expected to expand no more than 0.001 in./in. of cross-section when quenched in air from the proper hardening temperature.

IMPACT PROPERTIES

To determine impact properties, unnotched Charpy impact specimens were selected. They were machined over-size, heat-treated, and finish-ground to 0.250 in x 0.375 in x 2.165in. The heat treatment consisted of preheating at 1300F, and tempering at increasing temperatures.

Tempering
Temperatures °F
Hardness
Rockwell C
Unnotched
Charpy
Specimens (ft., lbs.)
400 58 180
500 56 227
600 55 228
700 54 199
800 53 179
900 52 190
1000 51 230
1100 46 264* (no break)
1200 39 264* (no break)
1300 33 264* (no break)

Maximum impact value obtained on impact testing machine.


Special Steel classification:

Stainless steel,Hi-Steel HSLA-80,Steel mould,Heat resistant steel,Tool Steel,Ball bearing

steel,Spring steel,Alloy steel,Construction steel,Die steel,Mould steel.

Product description:

Step Shaft AISI S7  Tube AISI S7  Pie-shaped AISI S7  Ring AISI S7  Module AISI S7  Large

valves of the main AISI S7  Other Profiled forgings AISI S7

Products Introduction  :

Specialized and high quality steel.

We have the advantages of equipment, technologies and price.

Specifications

Round bar :
Diameter : 1mm-2000mm

Square bar:
Size: 50mm * 50mm-600mm *600mm

Plate steel/flat bar:
Size:Thickness:0.1mm-800mm Width:10mm to 1500mm

Tube/pipe:
Size:OD:6-219mm  WT:1-35 mm.

Cold-rolled sheet:Thickness:2-5mm Width:1000mm Length:2000mm
Hot-rolled sheet:Thickness:6-80mm Width:210-610mm

Length: We can supply any length based on the customer's requirement.

Forging/hot rolling/ extrusion of steel.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching

+ tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on

the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable

electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the

customer's requirement

Excellent service for all kinds of industries,with advantages of technologies, equipment and

price.

We serve you with our honesty, integrity, and professionality.
 

Stainless Steel Suppliers | Hi-Steel HSLA-80 | Steel mould | Heat resistant steel | Tool Steel | Ball bearing steel | Spring steel | Alloy

Copyright 2003 - 2011 China longhai special steel Co., LTD is mainly engaged in all kinds of stainless steel 630 production, wholesale, retail enterprises

TEL:+86-15328239557 | FAX:+86-816-3639422 | E-mail:sales@specialsteel-jy.com | Add:119#,Jiangdong road, Sanhe Town,Jiangyou City, Sichuan Province, China | Zip:621701