Product categories
More »
Stainless Steel
Stainless Steel specifications held in the austenitic, martensitic and precipitation hardening varieties. Stocks are held in British Standard and International standards. Below is listed our most commonly supplied grades; please contact our sales office. Also stock is 301 stainless spring temper rolled strip.
Hi-Steel HSLA-80
Hi - Speed, high Speed Steel Tool Steel (made) : highly processed into the Tool Steel, carbon content high, while containing cr quantity is low (about 4%), reason burnish of Steel surface gloss darker, after heat can reach by HRc62 high hardness, resistance to rust performance not on a roll.
Mould Steel
Steel mould and Steel mould suppliers, global delivery, stock supply Steel mould steels.
Heat Resistant Steel
Heat resistant steel. AS Orlov Izobret. Mashinostr. 3, 48-49, 7/2000. The purpose of this work was to increase plasticity of heat resistant steel after aging at the 500-1300 deg C temperature and to improve its operational reliability.
Tool Steel
Comprehensive stocks held of tool steel, including hot work, cold work and plastic mould tool steel specifications. Below we detail our most common grades. Other British Standard and international special steels and tool steels are also available, please contact our sales office.
Ball Bearing Steel
Supplies Ball bearing steel of all types, along with carbon steel and specialty balls, to OEM's around the world. Also offers platinum balls, brass balls, gold, titanium, aluminum, carbon and plastic balls.
Spring Steel
Carbon spring steel is held in a wide range of sizes. Detailed below are our most common specifications. Carbon steel strip and spring steel sheet is available most commonly in the hardened and tempered condition, though certain sizes are available in the annealed condition. Round and flat bar is stocked in the as rolled condition. Most spring steel specifications are held to British Standard steel specifications including BS1449 & BS970.
Alloy and Carbon Steel
Alloy steel is steel alloyed with a variety of elements in total amounts of between 1.0% and 50% by weight to improve its mechanical properties. Alloy steels are broken down into two groups: low alloy steels and high alloy steels. The difference between the two is somewhat arbitrary: Smith and Hashemi define the difference at 4.0%, while Degarmo, et al., define it at 8.0 %.[1][2] Most commonly, the phrase "alloy steel" refers to "low alloy" steels.
News
More »
Enterprise email
Home » Stainless Steel » Product introduction
CA15 Stainless Steel
- Numbers: 2011092135
- Model: CA15
- Producers: China
- Update time: 2011.09.22
- Browse:
Product Description:
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell C | <= 23.0 | <= 23.0 | |
| Tensile Strength, Ultimate | >= 690 MPa | >= 100000 psi | |
| Tensile Strength, Yield | >= 520 MPa | >= 75400 psi | |
| Elongation at Break | >= 17.0 % | >= 17.0 % | |
| Component Elements Properties | Metric | English | Comments |
| Carbon, C | <= 0.15 % | <= 0.15 % | |
| Chromium, Cr | 11.5 - 14.0 % | 11.5 - 14.0 % | |
| Copper, Cu | <= 0.50 % | <= 0.50 % | |
| Iron, Fe | 77.6 - 84.6 % | 77.6 - 84.6 % | As remainder |
| Manganese, Mn | <= 1.0 % | <= 1.0 % | |
| Molybdenum, Mo | 0.40 - 1.0 % | 0.40 - 1.0 % | |
| Nickel, Ni | 3.50 - 4.50 % | 3.50 - 4.50 % | |
| Phosphorous, P | <= 0.040 % | <= 0.040 % | |
| Silicon, Si | <= 1.0 % | <= 1.0 % | |
| Sulfur, S | <= 0.030 % | <= 0.030 % | |
| Tungsten, W | <= 0.10 % | <= 0.10 % | |
| Vanadium, V | <= 0.050 % | <= 0.050 % | |
Users viewing this material also viewed the following:
ASTM A487 (CA15M)
ASTM A743/A743M(98) (CA15)
ASTM A352/A352M(98) (CA6NM)
CA6NM Cast Stainless steel
ASTM A743/A743M(98) (CA6NM)
MQCCA15B10 / 13330
Our products meet Chinese GB, Japanese JIS, US ASTM, UK BS, EU DIN standards and so on.
Diameter : 1mm-2000mm
Size: 50mm * 50mm-600mm *600mm
Size: Thickness: 0.1mm-800mm Width: 10mm to 1500mm
Size: OD: 6-219mm WT: 1-35 mm.