Product categories

More »

Stainless Steel

Stainless Steel specifications held in the austenitic, martensitic and precipitation hardening varieties. Stocks are held in British Standard and International standards. Below is listed our most commonly supplied grades; please contact our sales office. Also stock is 301 stainless spring temper rolled strip.

Hi-Steel HSLA-80

Hi - Speed, high Speed Steel Tool Steel (made) : highly processed into the Tool Steel, carbon content high, while containing cr quantity is low (about 4%), reason burnish of Steel surface gloss darker, after heat can reach by HRc62 high hardness, resistance to rust performance not on a roll.

Mould Steel

Steel mould and Steel mould suppliers, global delivery, stock supply Steel mould steels.

Heat Resistant Steel

Heat resistant steel. AS Orlov Izobret. Mashinostr. 3, 48-49, 7/2000. The purpose of this work was to increase plasticity of heat resistant steel after aging at the 500-1300 deg C temperature and to improve its operational reliability.

Tool Steel

Comprehensive stocks held of tool steel, including hot work, cold work and plastic mould tool steel specifications. Below we detail our most common grades. Other British Standard and international special steels and tool steels are also available, please contact our sales office.

Ball Bearing Steel

Supplies Ball bearing steel of all types, along with carbon steel and specialty balls, to OEM's around the world. Also offers platinum balls, brass balls, gold, titanium, aluminum, carbon and plastic balls.

Spring Steel

Carbon spring steel is held in a wide range of sizes. Detailed below are our most common specifications. Carbon steel strip and spring steel sheet is available most commonly in the hardened and tempered condition, though certain sizes are available in the annealed condition. Round and flat bar is stocked in the as rolled condition. Most spring steel specifications are held to British Standard steel specifications including BS1449 & BS970.

Alloy and Carbon Steel

Alloy steel is steel alloyed with a variety of elements in total amounts of between 1.0% and 50% by weight to improve its mechanical properties. Alloy steels are broken down into two groups: low alloy steels and high alloy steels. The difference between the two is somewhat arbitrary: Smith and Hashemi define the difference at 4.0%, while Degarmo, et al., define it at 8.0 %.[1][2] Most commonly, the phrase "alloy steel" refers to "low alloy" steels.

News

More »

Enterprise email

Home » Alloy and Carbon Steel » Product introduction

Din 2.4066/2.4068 Alloy Steel

  • Numbers: 2011070601
  • Model: Din 2.4066/2.4068
  • Producers: China
  • Update time: 2011.07.06
  • Browse:

Product Description:

Ni-base Alloy steel

Din 2.4066/2.4068 Ni-base Alloy Steel

Nickel 200/201 UNS N02200/N02201 NA 11/NA12

Introdution:
Din 2.4066 and Din 2.4068 are solid solution strengthened, commercially pure wrought materials with good mechanical properties over a wide range of temperatures and excellent resistance to many corrosives, in particular hydroxides. Din 2.4066 was a modification of  Din 2.4066/2.4068  to control carbon (.02 max) which keeps it from being embrittled by intergranular precipitates at temperatures of 600° F to 1400° F in many processes. Typically, the elemental restrictions of both, Din 2.4066/2.4068 , are combined into one, dual-certified chemistry resulting in a single alloy with the desired characteristics of both alloys, Din 2.4066/2.4068.

Characteristics:
1. Highly resistant to various reducing chemicals
2. Excellent resistance to caustic alkalies
3. High electrical conductivity
4. Excellent corrosion resistance to distilled and natural waters
5. Resistance to neutral and alkaline salt solutions
6. Excellent resistance to dry fluorine
7. Widely used to handle caustic soda
8. Good thermal, electrical and magnetostrictive properties
9. Offers some resistance to hydrochloric and sulfuric acids at modest temperatures and concentrations

Both Din 2.4066 and Din 2.4068 offer corrosion resistance in reducing and neutral media as well as in oxidizing atmospheres provided that the oxidizing media allows the formation of a passive oxide film. This oxide film accounts for the materials excellent resistance in caustic environments. Corrosion rates in both marine and rural atmospheres are very low. The resistance of Din 2.4066/2.4068 to corrosion by distilled and natural waters is excellent. Plus it also gives excellent service in flowing sea water even at high velocity, but in stagnant or very low-velocity sea water severe local attack may occur under fouling organisms or other deposits. In hot water systems where the steam contains carbon dioxide and air in certain proportions, corrosion rates will be initially high but will decrease with time if conditions favor the formation of a protective film.
Din 2.4066 is normally limited to service at temperatures below 600° F. At higher temperatures  Din 2.4066 Products can suffer from graphitization which can result in severely compromised properties. When operating temperatures are expected to exceed 600° F, carbon content becomes critical. The lower carbon content of  Din 2.4068 makes the material resistant to graphitization and therefore less subject to embrittlement. Din 2.4066/2.4068 are approved for construction of pressure vessels and components under ASME Boiler and Pressure Vessel Code Section VIII, Division 1. Din 2.4066 is approved for service up to 600° F while Din 2.4068 is approved for service up to 1230° F. Melting point is 2615-2635° F.

Available Form:
Sheet , Plate, Bar, Pipe & Tube (welded & seamless) , Fittings (i.e. flanges, slip-ons, blinds, weld-necks, lapjoints, long welding necks, socket welds, elbows, tees, stub-ends, returns, caps, crosses, reducers, and pipe nipples) , Wire.

Application:
1. Food processing equipment
2. Marine and offshore engineering
3. Salt production
4. Caustic handling equipment
5. Manufacture and handling of sodium hydroxide, particularly at temperatures above 300° F
6. Reactors and vessels in which fluorine is generated and reacted with hydrocarbons
Applications where Din 2.4066/2.40681 can be used include chemical processing and storage, synthetic fiber production, and processes where sodium hydroxide and fluorine is used. Other applications include aerospace and defense as well as food processing. Din 2.4066/2.4068 has exceptional resistance to caustic alkalies at various temperatures and concentrations.


Fabrication with Din 2.4066/2.4068
All hot working and cold working practices can be utilized when shaping Din 2.4066/2.4068. Hot working temperatures should be between 1200° F and 2250° F with heavy forming to be performed at temperatures above 1600° F. Annealing should be performed at a temperature between 1300° F and 1600° F. Care should be taken when choosing the anneal temperature and time at temperature for this can greatly influence the mechanical properties and structure of the material.
Din 2.4066/2.4068 can be easily welded by conventional welding, brazing, and soldering processes with the exception of the oxyacetylene process.
 

Product description:

Step Shaft Din 2.4066/2.4068  Tube Din 2.4066/2.4068  Pie-shaped Din 2.4066/2.4068  Ring Din 2.4066/2.4068   Module Large valves of the main Din 2.4066/2.4068   Other Profiled forgings Din 2.4066/2.4068

Special Steel classification:

Stainless steel, Hi-Steel HSLA-80, Mould steel,  Heat resistant steel, Tool steel, Ball bearing steel,Spring steelAlloy steel,  Construction steel,  Die steel, High-speed steel,  angles, channels, H steel, I-beams, welded pipes, seamless tubes,

Standard:
Our products meet Chinese GB, Japanese JIS, US ASTM, UK BS, EU DIN standards and so on.

Our advantages:

Our advantages such as advanced management and operation concepts, suitable work facilities, highly qualified talents and a number of trade partners who have long-term and close cooperation with us have ensured us to provide global customers with competitive high-quality commodities and excellent services, quickly, accurately, conveniently and completely.

Products Introduction:

Specifications

Round bar:
Diameter : 1mm-2000mm

Square bar:
Size:  50mm * 50mm-600mm *600mm

Plate steel/flat bar:
Size: Thickness:  0.1mm-800mm Width: 10mm to 1500mm

Tube/pipe:
Size: OD:  6-219mm  WT: 1-35 mm.

Cold-rolled sheet: Thickness:  2-5mm Width:1000mm Length: 2000mm

Hot-rolled sheet: Thickness:6-80mm Width: 210-610mm

Length:  We can supply any length based on the customer's requirement.

Forging/hot rolling/ extrusion of steel.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Finished goods condition:  hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement


Surface conditions:  scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing:  electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection:  100% ultrasonic inspection for any inperfections or based on the customer's requirement

Excellent service for all kinds of industries, with advantages of technologies,  equipment and price.

We serve you with our honesty,  integrity,  and professionality.

Stainless Steel Suppliers | Hi-Steel HSLA-80 | Steel mould | Heat resistant steel | Tool Steel | Ball bearing steel | Spring steel | Alloy

Copyright 2003 - 2011 China longhai special steel Co., LTD is mainly engaged in all kinds of stainless steel 630 production, wholesale, retail enterprises

TEL:+86-15328239557 | FAX:+86-816-3639422 | E-mail:sales@specialsteel-jy.com | Add:119#,Jiangdong road, Sanhe Town,Jiangyou City, Sichuan Province, China | Zip:621701